Product Description
TOPAS 8007F-04 is a general purpose film extrusion grade. It is a high clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and healthcare applications. It is used in monolayer cast applications, and in coextrusions in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as blister, twist, barrier, shrink and easy tear packaging. Industrial uses include formed decorative sheet products. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended.

Selected Applications

• Pharmaceutical blisters

• Deep draw barrier trays

• Shrink films and labels

• Twist films

• Decorative sheet

• Food packaging

• Healthcare and food contact

Leading Attributes

• Clarity, forming, barrier, purity, halogen-free

• Excellent deep forming, unlike other barriers

• High shrink, low stress, gloss, clarity, toughness

• High gloss, outstanding deadfold, clean cutting

• Gloss, hardness, chemical resistance, forming

• Not manufactured with BPA, phthalates, or halogens

• Broad regulatory compliance

Related Grades for Packaging and Film Extrusion

• TOPAS 8007F-400 - robust extrusion grade especially for PE blends

• TOPAS 8007F-600 - robust clarity extrusion grade especially for PE blends

TOPAS? 8007F-04 物性表

基本信息
特性	純度高 防潮 剛性，高 高光 共聚物 耐化學性良好 清晰度，高 韌性良好 食品接觸的合規(guī)性 通用 無 BPA 無定形的 無鹵
用途	包裝 薄膜 標簽 流延薄膜 片材 食品包裝 通用 藥品包裝 醫(yī)療/護理用品
機構(gòu)評級	DMF 12132 FDA FCN 405 歐洲 10/1/2011 12:00:00 AM
形式	粒子
加工方法	薄膜擠出 吹塑薄膜 共擠薄膜 流延薄膜 熱成型

物理性能	額定值	單位制	測試方法
密度	1.02	g/cm3	ISO 1183
熔流率（熔體流動速率）			ISO 1133
190°C/2.16 kg	1.8	g/10 min	ISO 1133
230°C/2.16 kg	11	g/10 min	ISO 1133
溶化體積流率（MVR）			ISO 1133
190°C/2.16 kg	2.00	cm3/10min	ISO 1133
230°C/2.16 kg	12.0	cm3/10min	ISO 1133
吸水率(飽和, 23°C)	0.010	%	ISO 62

薄膜	額定值	單位制	測試方法
薄膜厚度 - 經(jīng)測試	70	μm
拉伸模量			ISO 527-3/1
MD : 70 μm, 鑄造薄膜	2200	MPa	ISO 527-3/1
TD : 70 μm, 鑄造薄膜	1800	MPa	ISO 527-3/1
拉伸應力			ISO 527-3/50
MD : 斷裂, 70 μm, 鑄造薄膜	57.0	MPa	ISO 527-3/50
TD : 斷裂, 70 μm, 鑄造薄膜	50.0	MPa	ISO 527-3/50
伸長率			ISO 527-3/50
MD : 斷裂, 70 μm, 鑄造薄膜	2.9	%	ISO 527-3/50
TD : 斷裂, 70 μm, 鑄造薄膜	3.0	%	ISO 527-3/50
落錘沖擊(70 μm, 鑄造薄膜)	36	g	ISO 7765-1
埃爾曼多夫抗撕強度			ISO 6383-2
MD : 70 μm, 鑄造薄膜	2.2	N	ISO 6383-2
TD : 70 μm, 鑄造薄膜	2.3	N	ISO 6383-2
透氧率(23°C, 70 μm, 擠塑薄膜, 50% RH)	25	cm3·mm/m2/atm/24 hr	ASTM D3985
水氣透過率(70 μm, 23°C, Cast Film, 85% RH)	0.094	g·mm/m2/atm/24 hr	ASTM F1249

熱性能	額定值	單位制	測試方法
玻璃轉(zhuǎn)化溫度	78.0	°C	ISO 11357-2

光學性能	額定值	單位制	測試方法
光澤度(60°, 70.0 μm, 鑄造薄膜)	100		ISO 2813
霧度(70.0 μm, 鑄造薄膜)	1.0	%	ISO 14782

擠出	額定值	單位制
擠塑機進料部分	20 到 60	°C
擠出機螺桿長徑比L / D	28:1
料筒1區(qū)溫度	210 到 220	°C
料筒2區(qū)溫度	230 到 240	°C
料筒3區(qū)溫度	230 到 240	°C
料筒4區(qū)溫度	230 到 240	°C
口模溫度	230 到 240	°C