英菲力TPV-ENFLEX-V1045A
價格
訂貨量(公斤)
¥39.00
≥25
店鋪主推品 熱銷潛力款
잵잰잳잭잲잭잵잯잲잭잭
在線客服
General | ||||
Material Status |
| |||
Availability |
| |||
Features |
| |||
Appearance |
| |||
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
Density / Specific Gravity | ASTM D792 | ||
Elastomers | Nominal Value | Unit | Test Method |
Tensile Stress (100% Strain) | psi | ASTM D412 | |
Tensile Strength (Break) | psi | ASTM D412 | |
Tensile Elongation (Break) | % | ASTM D412 | |
Tear Strength 2 | lbf/in | ASTM D624 | |
Compression Set | ASTM D395 | ||
158°F, 22 hr | % | ||
257°F, 70 hr | % | ||
Hardness | Nominal Value | Unit | Test Method |
Durometer Hardness | ASTM D2240 | ||
Shore A, 5 sec, Extruded | |||
Shore A, 5 sec, Injection Molded | |||
Thermal | Nominal Value | Unit | Test Method |
Brittleness Temperature | °F | ASTM D746 | |
Melting Temperature | °F | ASTM D1238 |
TPV ENFLEX V1045A
TPV組成
許多塑料和橡膠之間可形成TPV,但僅有個別共混物經(jīng)過動態(tài)硫化后具有實用價值,商業(yè)化的有PP/PE/EPDM,PP/NBR,PP/ACM,PS/SEBS。在化工出版社《熱塑性彈性體》一書中對11種橡膠和9種塑料制備的99種橡膠/塑料共混物進行了評論,研究發(fā)現(xiàn),要得到最佳性能的橡膠/熱塑性塑料動態(tài)硫化共混物,必須滿足以下條件:
(1)塑料和橡膠兩種聚合物的表面能匹配;
(2)橡膠纏結分子鏈長度較低;
(3)塑料的結晶度大于15%。當塑料與橡膠之間的極性或表面能差別比較大的情況下,添加合適的相容劑,再進行動態(tài)硫化,也可以得到性能優(yōu)良的共混物。
1)注塑加工
TPV的熔體粘度比許多種普通熱塑性材料更大,在加工時,需應用較大的注料嘴、注料口、流道和澆口,還需要采用高的注射壓力和較快的注射速率,以提高充模速度和減少飛邊,此后在較高的壓力下有一個短的保持時間,使之足以將澆料口凍結。 注射螺桿的速度應當是100至200轉/分,背壓力在不需要混合時應當盡可能低。
2)擠塑加工
不需要真空定徑。建議采用長徑比為28比1或更大比例的擠塑機。通常單段螺桿比為3比1左右,如果需要用篩網(wǎng)組合,可用20至60網(wǎng)目的篩網(wǎng)。最好將熔體溫度保持在規(guī)定范圍的下限,使擠塑產(chǎn)品的質量最優(yōu)。
3)吹塑加工
TPV機械操作條件要求與注塑和擠塑所規(guī)定的相同。模具設計、型坯尺寸、加工周期時間、以及壁厚均勻等吹塑加工因素都與制件的幾何形狀有很大的關系。熔體加熱過度將使牽伸比下降,應當避免過熱。
交通器材
1、道路、橋梁伸縮縫;
2、道路安全設施、緩沖防撞部件;
3、集裝箱密封條。
建筑建材
1、動力部件密封條
2、建筑伸縮縫、密封條
3、供排水管密封件、水灌系統(tǒng)控制閥等